 日本神钢KOBELCO NO65G氩弧焊丝ER70S-2进口焊丝

NO65G TIG rod, equivalent to AWS A5.18 ER70S-2, contains less C, Si and Mn contents than TG-S50 or TG-S51T; instead, Al, Ti and Zr are specially added. These elements help to decrease the amount of oxygen in the molten pool, allowing NO65G to provide a weld bbbbl of relatively high cleanness. On the other hand, it is a little inferior to TG-S50 or TG-S51T in terms of fluidity of molten bbbbl, because of which its surface tension increases while the oxygen content in the molten bbbbl is decreased.

Because Al, Ti or Zr is an element with high oxygen affinity, slag can be generated on the bead surface after a part of the element combines with oxygen in the molten bbbbl during welding. Users are therefore advised to beware of weld defects, such as poor bead appearance or slag inclusion, caused by the slag.

Each chemical element in NO65G rod is strictly controlled to maintain a narrow range within the AWS A5.18 ER70S-2 specification so that it can meet the tough requirements set out by Japanese clients for mechanical properties in critical structural projects.

Table 8: Typical chemistry of weld bbbbl (mass%)天津海焊

C	Si	Mn	P	S	Cu	Al	Ti	Zr
0.04	0.50	1.20	0.007	0.012	0.22	0.06	0.05	0.02

Table 9: Typical mechanical properties of weld bbbbl

	Tensile test at RT			Absorbed energy (J)
	YS (MPa)	TS (MPa)	EI (%)	-40°C	-30°C	-20°C
As-welded	584	635	29	Av 165	Av 200	Av 215
625°C × 8hr	545	615	30	Av 138	Av 160	Av 175

Table 8, Table 9 and Figure 5 show the typical chemistry of NO65G weld bbbbl, the typical mechanical properties in as-welded and PWHT (625°C×8 hr) conditions and the absorbed energies in relat ion to the tes t temperatures, respectively.